product
s1150g
characteristic
● free of constituents such ashalogen antimony,red phosphorous etc..no txic gasemission and no hazardous residue during wastecombustion
● excellent mechanicalprocessibility and thermal resistance ,lead free processcompliancy.
application area
smartphone,tablet,nb,led,game station ,automotiveelectronics,communication equipmet
- product performance
- product certificate
- data download
| items | method | condition | unit | typical value | |
|---|---|---|---|---|---|
| tg | ipc-tm-650 2.4.25 | dsc | ℃ | 155 | |
| td | ipc-tm-650 2.4.24.6 | 5% wt. loss | ℃ | 355 | |
| cte（z-axis） | ipc-tm-650 2.4.24 | before tg | ppm/℃ | 40 | |
| after tg | ppm/℃ | 230 | |||
| 50-260℃ | % | 2.8 | |||
| cte（x/y-axis） | ipc-tm-650 2.4.24.5 | before tg | ppm/℃ | — | |
| t260 | ipc-tm-650 2.4.24.1 | tma | min | 60 | |
| t288 | ipc-tm-650 2.4.24.1 | tma | min | 45 | |
| thermal stress | ipc-tm-650 2.4.24.13 | 288℃, solder dip | -- |
>100s no delamination |
|
| volume resistivity | ipc-tm-650 2.5.17.1 | after moisture resistance | mω-cm | 1.15×108 | |
| e-24/125 | mω-cm | 4.13×108 | |||
| surface resistivity | ipc-tm-650 2.5.17.1 | after moisture resistance | mω | 9.61×106 | |
| e-24/125 | mω | 5.37×107 | |||
| arc resistance | ipc-tm-650 2.5.1 | d-48/50 d-4/23 | s | 178 | |
| dielectric breakdown | ipc-tm-650 2.5.6 | d-48/50 d-4/23 | kv | 45kv nb | |
| electrical strength | ipc-tm-650 2.5.6.2 | d-48/50 d-4/23 | kv/mm | — | |
| dissipation constant (dk) | ipc-tm-650 2.5.5.9 | 1ghz | -- | 4.5 | |
|
ipc-tm-650 2.5.5.9 |
1mhz | -- | 4.8 | ||
| dissipation factor (df) | ipc-tm-650 2.5.5.9 | 1ghz | -- | 0.011 | |
|
ipc-tm-650 2.5.5.9 |
1mhz | -- | 0.009 | ||
| peel strength(1oz hte copper foil) | ipc-tm-650 2.4.8 | a | n/mm | — | |
| after thermal stress 288℃,10s | n/mm | 1.5 | |||
| 125℃ | n/mm | — | |||
| flexural strength | lw | ipc-tm-650 2.4.4 | a | mpa | 630 |
| cw | ipc-tm-650 2.4.4 | a | mpa | 480 | |
| water absorption | ipc-tm-650 2.6.2.1 | e-1/105 d-24/23 | % | 0.10 | |
| thiermal conductivity | astm e1461 | z-axis | w/m·k | — | |
| flammability | ul94 | c-48/23/50 | rating | v-0 | |
| e-24/125 | rating | v-0 | |||
remarks:
1. specification sheet: ipc-4101/128, is for your reference only.
2. all the typical value is based on the 1.6mm specimen, whilethe tg is for specimen≥0.50mm.
3. all the typical value listed above is for your reference only, pleaseturn to shengyi technology co., ltd. for detailed information, and all rightsfrom this data sheet are reserved by shengyi technology co., ltd.
explanations: c=humidity conditioning, d=immersion conditioning indistilled water, e=temperature conditioning.
the figures following the letter symbols indicate with the firstdigit the duration of the preconditioning in hours, with the second digit thepreconditioning temperature in ℃ and with the third digit the relativehumidity.