product
autolad2g
characteristic
cti≥600vfor hash environment and critical design for safe creepage distance
highvoltage anti-caf
extremethermal cycling resistance
mot150℃(≥0.63mm)
application area
high power & high voltageapplications
pev& hev automotive electrification
onboard charger(obc), etc.
- product performance
- product certificate
- data download
| items | method | condition | unit | typical value |
|---|---|---|---|---|
| tg | 2.4.24.4 | dma | ℃ | 190 |
| 2.4.25d |
dsc |
175 | ||
| td | 2.4.24.6 | 5% wt. loss | ℃ | 402 |
|
t288 |
2.4.24.1 | tma | min | 60 |
| t260 |
2.4.24.1 |
tma |
min |
60 |
|
thermal stress |
2.4.13.1 |
288℃, solder dip |
- |
>100s no delamination |
| cte (z-axis) | 2.4.24 | before tg | ppm/℃ | 35 |
| after tg | ppm/℃ | 190 | ||
| 50-260℃ | % | 2.2 | ||
| dissipation constant (1ghz) | 2.5.5.9 | c-24/23/50 | - | 4.3 |
|
dissipation factor (1ghz) |
2.5.5.9 |
c-24/23/50 |
- | 0.015 |
| volume resistivity | 2.5.17.1 | c-96/35/90 | mω.cm | 4.83×107 |
|
surface resistivity |
2.5.17.1 |
c-96/35/90 | mω | 4.98×106 |
| arc resistance | 2.5.1 | d-48/50 d-0.5/23 | s | 130 |
| dielectric breakdown | 2.5.6 | d-48/50 d-0.5/23 | kv | 45 kv nb |
| peel strength (1oz) | 2.4.8 | 288℃/10s | n/mm | 1.3 [7.43] |
| flexural strength (lw/cw) | 2.4.4 | a | mpa | 520/400 |
| water absorption | 2.6.2.1 | e-1/105 d-24/23 | % | 0.09 |
|
flammability |
ul94 |
c-48/23/50 |
rating |
v-0 |
| cti | iec60112 | a | rating | plc0 |
remarks:
remark:
1. specificationsheet: ipc-4101/130, is for your reference only.
2. all the typicalvalue is based on the 1.6mm (8x7628) specimen, “ * ” is based on the1.0mm(9x2116) specimen.
3.inorder to satisfy cti≥600v,2116(rc≥54%)，7628(rc≥45%) or above thickness prepreg is suggestedto be used for outer prepreg layer. if you have any queries, please turn toshengyi technology co., ltd for detailed information.
4. all the typicalvalue listed above is for your reference only, please turn to shengyitechnology co., ltd for detailed information, and all rights from this datasheet are reserved by shengyi technology co., ltd.