product
autolad3g
characteristic
application area
specified for automotive electronics, including junction box, ecu inengine and body
- product performance
- product certificate
- data download
| items | method | condition | unit | typical value |
|---|---|---|---|---|
| tg | 2.4.24.4 | dma | ℃ | 200 |
|
2.4.24.3 |
tma | 180 | ||
| 2.4.25d |
dsc |
190 | ||
| td | 2.4.24.6 | 5% wt. loss | ℃ | 408 |
|
t288 |
2.4.24.1 | tma | min | >60 |
| t300 |
2.4.24.1 |
tma |
min |
>60 |
|
thermal stress (unetched/etched) |
2.4.13.1 |
288℃, 20s solder dip |
- |
pass/pass |
| cte (z-axis) | 2.4.24 | before tg | ppm/℃ | 35 |
| after tg | ppm/℃ | 180 | ||
| 50-260℃ | % | 1.8 | ||
| dissipation constant (10ghz) | 2.5.5.5 | c-24/23/50 | - | 4.0 |
|
dissipation factor (10ghz) |
2.5.5.5 |
c-24/23/50 |
- | 0.013 |
| volume resistivity | 2.5.17.1 | e-24/125 | mω.cm | 5.0×106 |
|
surface resistivity |
2.5.17.1 |
e-24/125 | mω | 2.0×108 |
| arc resistance | 2.5.1 | d-48/50 d-0.5/23 | s | 160 |
| dielectric breakdown | 2.5.6 | d-48/50 d-0.5/23 | kv | 45 kv nb |
| peel strength (1oz) | 2.4.8 | 288℃/10s | n/mm | 1.3 [7.43] |
| flexural strength (lw/cw) | 2.4.4 | a | mpa | 560/450 |
| water absorption | 2.6.2.1 | e-1/105 d-24/23 | % | 0.13 |
|
flammability |
ul94 |
c-48/23/50 |
rating |
v-0 |
| cti | iec60112 | a | rating | plc3 |
remarks:
remark:
1. all the typical value is based onthe 1.6mm (8*7628) specimen. the dk and df value is based on 57% rc.
2. all the typical value listed above isfor your reference only, please turn to shengyi technology co., ltd fordetailed information, and all rights from this data sheet are reserved by shengyitechnology co., ltd.
explanations:c=humidity conditioning; d=immersion conditioning in distilled water;e=temperature conditioning.
the figures following the letter symbolsindicate with the first digit the duration of the preconditioning in hours,with the second digit the preconditioning temperature in ℃ and with the third digit the relative humidity.