product
sdi03k
characteristic
● lead free compatible.
● high tg halogen free, tg 175℃ (tma)
● uv blocking/aoi compatible.
● lower z-axis cte.
application area
● smartphone, notebook, tablet
● instrument, vcr, tv
● game station
● communication equipment
- product performance
- product certificate
- data download
items | method | condition | unit | typical value |
---|---|---|---|---|
tg | 2.4.24.4 | dma | ℃ | 200 |
2.4.24 | tma | 175 | ||
td | 2.4.24.6 | 5% wt. loss | ℃ | 390 |
t288 |
2.4.24.1 | tma | min |
>60 |
t260 |
2.4.24.1 |
tma |
min |
>60 |
thermal stress |
2.4.13.1 |
288℃, solder dip |
- | pass |
cte (z-axis) | 2.4.24 | before tg | ppm/℃ | 40 |
after tg | ppm/℃ | 230 | ||
50-260℃ | % | 2.3 | ||
dissipation constant (1ghz) | 2.5.5.9 | c-24/23/50 | - | 3.47 |
dissipation factor (1ghz) |
2.5.5.9 |
c-24/23/50 |
- | 0.0083 |
volume resistivity | 2.5.17.1 | c-96/35/90 | mω.cm | 4.76×108 |
surface resistivity |
2.5.17.1 |
c-96/35/90 | mω | 1.84×107 |
arc resistance | 2.5.1 | d-48/50 d-0.5/23 | s | 181 |
dielectric breakdown | 2.5.6 | d-48/50 d-0.5/23 | kv | >45 |
peel strength (h oz) |
2.4.8 |
288℃/10s |
n/mm |
1.0 |
flexural strength (lw/cw) |
2.4.4 |
a |
mpa |
510/490 |
water absorption | 2.6.2.1 | e-1/105 d-24/23 | % | 0.07 |
flammability |
ul94 |
c-48/23/50 |
rating |
v-0 |
remarks:
1. all the typical value is based on the 1.0mm specimen, while the tg is for specimen≥0.50mm, and the dielectric strength is based on other thickness specimen mentioned above.2. all the typical values listed above are for your reference only and not intended for specification. please contact shengyi technology co., ltd. for detailed information. all rights from this data sheet are reserved by shengyi technology co., ltd.
explanation: c=humidity conditioning, d=immersion conditioning in distilled water, e=temperature conditioning
the first digit following the letter indicates the duration of preconditioning in hours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.